1. The quality of heat treatment of aluminum extrusion die directly affects the service life of the extrusion die. Quenching is to improve the hardness of the mold, and repeated tempering is to improve the toughness of the mold and stabilize the internal structure. The hardness value of mold heat treatment is specified: large aluminum extrusion die (F>500mm), HRC45-48; Mowld canolig (F300 ~ 500mm), HRC47-50; Mae allwthio bach yn marw (f<300mm), HRC48-51; Three points are tested on the same plane of a set of molds, and the hardness value of each point should be qualified within the specified range.
2. Dylid rhoi sylw arbennig i sawl pwynt yn y broses trin gwres o allwthio marw:
a. Dylai cyflymder gwresogi'r adran tymheredd uchel fod yn gyflym, ac ni ddylai'r amser dal fod yn rhy hir, er mwyn atal yr allwthio rhag marw rhag gorboethi neu orboethi, gorboethi - grawn bras, gorboethi - bydd elfennau pwynt toddi isel a chynhwysiadau yn achosi diddymu;
b. Ar ôl diffodd, dylid tymeru'r marw allwthio alwminiwm mewn pryd i atal craciau;
c. Pan ganfyddir nad yw caledwch yr allwthio marw yn annigonol neu'n anwastad ar ôl triniaeth wres, dylid anelio, a dylid ail-gario'r driniaeth wres yn unol â'r broses (pan fydd y gwerth caledwch yn
d. Ar gyfer mowldiau allwthio alwminiwm mawr neu fowldiau gorffenedig gyda cheudodau cymhleth, dylid ychwanegu proses dymheru sy'n lleddfu straen (i ddileu prosesu trydanol a straen peiriannu, hynny yw, i ddileu straen thermol a straen microstrwythur);
e. Dylai tymheredd olew quenching y mowld fod yn 100 gradd i sicrhau'r effaith quenching.